Sleeve bearing arrangement

ABSTRACT

There is provided a maintenance-free sleeve bearing arrangement that is light in weight, has a long service life and does not require resupply of oil during operation. The sleeve bearing arrangement is comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing formed of CRB ceramics, and/or the shaft formed of the CRB ceramics are used.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The invention relates to a sleeve bearing arrangement using a new material, and more particularly, the invention provides a maintenance-free sleeve bearing that does not require resupply of oil during operation. At the same time, it is an object of the invention to provide a sleeve bearing using a high-tech eco-material (state-of-the-art material excellent in ecological adaptability) obtained from biomass type resources, different from conventional industrial material.

[0003] 2. Description of the Related Art

[0004] In the past, sleeve bearings made of resin such as polyacetal, polyamide, etc. have been in use for rotating parts which are light in weight and slow in rotation speed because such sleeve bearings are available at a low cost in comparison with sleeve bearings made of metal.

[0005] However, as a lubricating oil is required between a shaft and a sleeve bearing, a method of lengthening a service life of the sleeve bearing has been under study. There are available various methods such as a method of increasing an mount of oil by increasing a volume of a shaft impregnated with oil, a method of replenishing oil by providing an oil pan, a method of preventing spilling of oil by devising an oil seal, and so forth. However, any of these methods has both merits and demerits, and there is room left for improvement.

SUMMARY OF THE INVENTION

[0006] The inventor of the present invention has conducted intense studies, and found out that a porous material is obtained by a process comprising the steps of mixing degreased bran derived from rice bran with a thermosetting resin before kneading, subjecting a kneaded mixture to a primary firing in an inert gas at a temperature in a range of 700 to 1000° C., pulverizing the kneaded mixture obtained after the primary firing into carbonized powders sieved through mesh 100, mixing the carbonized powders with a thermosetting resin before kneading, pressure-forming a kneaded mixture thus obtained at a pressure in a range of 20 to 30 MPa, and applying a heat treatment again to a formed kneaded mixture in the inert gas at a temperature in a range of 100 to 1100° C., and the porous material thus obtained (referred to hereinafter as CRB ceramics) has ideal characteristics as material suitable for use in sleeve bearings.

[0007] Further, it has been found that the CRB ceramics described above are insusceptible to damage, light in weight, and has a long service life, having in addition ability to retain oil and grease for a long period of time. It has also been found that the porous material has not only the ideal characteristics as the material suitable for use in the sleeve bearings but also a small contraction ratio of the dimensions of a formed workpiece formed thereof to those of a finished product.

[0008] More specifically, the porous material described above has the contraction ratio of the dimensions of the formed workpiece formed thereof to those of the finished product, as small as 3% or less, 13 wt % of oil retention characteristic, 4.85×10⁻³ Ω cm of volume resistivity, and density in a range of 1.05 to 1.3 g/cm³, and further, it has been possible to obtain the porous material having suitable hardness, and still friction coefficient in the order of about 0.15 after fired at a high temperature.

[0009] The inventor of the present invention has found out that it is possible to fabricate a sleeve bearing arrangement, having diverse characteristics, by forming a sleeve bearing from the porous material (the CRB ceramics) obtained by the process comprising the steps of mixing degreased bran derived from rice bran with a thermosetting resin before kneading, subjecting a kneaded mixture to a primary firing in an inert gas at a temperature in a range of 700 to 1000° C., pulverizing the kneaded mixture obtained after the primary firing into carbonized powders sieved through a screen of 100-mesh, mixing the carbonized powders with a thermosetting resin before kneading, pressure-forming a kneaded mixture thus obtained at a pressure in a range of 20 to 30 MPa, and applying a heat treatment again to a formed kneaded mixture in the inert gas at a temperature in a range of 100 to 1100° C., or by combining a conventional sleeve bearing formed of a synthetic resin or a steel-based metal with a shaft formed of the CRB ceramics. First, a typical sleeve bearing arrangement is shown in FIG. 1 wherein reference numeral 1 denotes a shaft, and reference numeral 2 denotes a sleeve bearing.

[0010] With the present invention, the shaft 1, and/or the sleeve bearing 2 are formed of the CRB ceramics.

BRIEF DESCRIPTION OF THE DRAWING

[0011]FIG. 1 is a sectional view of a typical embodiment of a sleeve bearing arrangement according to the invention, showing a shaft 1 and a sleeve bearing 2.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012] Degreased bran derived from rice bran, used in carrying out the present invention, may be either of domestic origin or of foreign origin, regardless of the kind of rice.

[0013] Further, any thermosetting resin may be used as long as it has thermosetting property, and typically cited as a thermosetting resin are a phenol resin, diaryl phthalate resin, unsaturated polyester resin, epoxy resin, polyimide resin, and triazine resin. In particular, the phenol resin is preferably used.

[0014] Furthermore, a thermoplastic resin such as polyamide, and so forth can be used in combination with a thermosetting resin provided that it is done without departing from the spirit and scope of the invention.

[0015] A mixing ratio of the degreased bran to a thermosetting resin is 50˜90:50˜10 by weight, however, a mixing ratio of 75:25 is preferably used.

[0016] For the thermosetting resin used in this case, one in a liquid state, having a relatively small molecular weight, is desirable.

[0017] A primary firing is applied at a temperature in a range of 700 to 100° C. using normally a rotary kiln for firing time in a range of 40 to 120 minutes.

[0018] A mixing ratio of carbonized powders after the primary firing to a thermosetting resin is 50˜90:50˜10 by weight, however, a mixing ratio of 75:25 is preferably adopted.

[0019] A kneaded mixture of the carbonized powders after the primary firing and the thermosetting resin is pressure-formed at a pressure in a range of 20 to 30 MPa, preferably in a range of 21 to 25 MPa. A mold is preferably at a temperature of about 150° C.

[0020] A heat treatment is applied at a temperature in a range of 600 to 1100° C. normally in a well-controlled electric furnace. Firing time is in a range of about 60 to 360 minutes.

[0021] A warming rate up to a temperature for the primary firing is required to be relatively moderate up to 500° C. In terms of more specific values, the warming rate is in a range of 0.5 to 2° C./min, preferably 1° C./min.

[0022] Further, in lowering the temperature of the kneaded mixture after baked, a relatively moderate cooling rate is required up to 500° C. Upon the temperature dropping to 500° C. or lower, the kneaded mixture is left to cool by itself. In terms of more specific values, a cooling rate is in a range of 0.5 to 4° C./min, preferably at 1° C./min.

[0023] Further, for an inert gas, any of helium, argon, neon, and nitrogen gas may be used, however, nitrogen gas is preferably used.

[0024] Further, with the present invention, a steel-based metal for use in a shaft or a sleeve bearing may be any of alloys composed of steel and nickel, chromium, molybdenum, or so forth, respectively, provided that it is an alloy hard, and resistant to rust.

[0025] Furthermore, for a synthetic resin for use in a shaft or a sleeve bearing, it is possible to use any synthetic resin that is reasonably hard and strong, that is, polyolefin such as hard polyethylene, polypropylene, and so forth, polyamide such as Nylon 66, polycarbonate, and so forth.

[0026] Embodiments of the invention are summed up as follows:

[0027] (1) An bearing arrangement comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing is formed of CRB ceramics;

[0028] (2) An bearing arrangement as set forth in item (1) above, wherein the shaft is formed of a steel-based metal;

[0029] (3) An bearing arrangement as set forth in item (1) above, wherein the shaft is formed of a synthetic resin;

[0030] (4) An bearing arrangement as set forth in item (1) above, wherein the shaft is formed of the CRB ceramics;

[0031] (5) An bearing arrangement comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing is formed of a steel-based metal, and the shaft is formed of CRB ceramics; and

[0032] (6) An bearing arrangement comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing is formed of a synthetic resin, and the shaft is formed of CRB ceramics.

[0033] Subsequently, the invention is further described in detail hereinafter based on preferred embodiments thereof, however, it is to be understood that the scope of the invention is not limited to the preferred embodiments in any way.

[0034] Production of Material for the Shaft and the Sleeve Bearing

[0035] The CRB ceramics were produced under the conditions of Table 1 shown below, and shafts of 2.98 mm (diameter)×20 mm (length) and sleeve bearings 5 mm long with the inside diameter 3.00 mm and the outside diameter 5.00 mm for housing the shaft therein were formed of the CRB ceramics. TABLE 1 conv. ex. 1 ex. 2 ex. 3 ex. 4 ex. 5 ex. 6 ex. 7 ex. mix. amt. (g) degr'd 75 75 75 80 60 55 85 75 bran t-sett. 25 25 25 20 40 35 15 25 resin prim. 900 900 900 850 1000 1000 800 — firing (° C.) 60 60 60 60 70 70 60 time (min) aver. 90 90 90 40 120 50 130 — particle size (μm) mix. amt. (g) c. powder 75 75 75 75 75 80 85 — t-sett. 25 25 25 25 25 20 15 resin form. 21.5 22.5 24.5 23.5 29.5 20.5 23.5 23.5 press. MPa heat 900 200 300 800 1000 1100 900 900 treat. (° C.) firing 120 100 130 120 100 90 120 120 time (hr.) warm. 1 1.5 1 1.5 2 1 1 1 rate cool. 2 left to left to 2 3 2 2 2 rate cool cool atm. nitro- nitro- nitro- nitro- nitro- nitro- nitro- nitro- gen gen gen gen gen gen gen gen

[0036] Embodiments

[0037] Fabrication of Sleeve Bearing Arrangements

[0038] shafts and sleeve bearings, formed of steel, shafts and sleeve bearings, formed of Nylon 66, and a diester type lubricating oil are prepared. These shafts and sleeve bearings were used in various combinations with the shafts and sleeve bearings formed of the CRB ceramics, respectively, fabricating sleeve bearing arrangements shown in Table 2. TABLE 2 sleeve bearing shaft embodiment 1 fabrication example 1 steel embodiment 2 fabrication example 2 steel embodiment 3 fabrication example 3 Nylon 66 embodiment 4 fabrication example 4 polycarbonate embodiment 5 fabrication example 3 fabrication example 1 embodiment 6 fabrication example 5 polyester embodiment 7 Nylon 66 fabrication example 2 embodiment 8 polypropylene fabrication example 7 embodiment 9 steel fabrication example 6 embodiment 10 fabrication example 1 fabrication example 7 comparative example 1 Nylon 66 steel

[0039] Tests were conducted on the sleeve bearing arrangement fabricated according to the respective embodiments, and test results are shown in Table 3. TABLE 3 lubricant lubricant retention after retention after 100 hrs. 1000 hrs overall ranking embodiment 1 ⊚ ◯ ◯ embodiment 2 ⊚ ◯ ◯ embodiment 3 ⊚ ◯ ◯ embodiment 4 ⊚ ◯ ◯ embodiment 5 ⊚ ⊚ ⊚ embodiment 6 ⊚ ◯ ◯ embodiment 7 ⊚ ◯ ◯ embodiment 8 ⊚ ◯ ◯ embodiment 9 ⊚ ◯ ◯ embodiment 10 ⊚ ⊚ ⊚ comparative Δ X X example 1

COMPARATIVE EXAMPLE

[0040] For the sake of comparison, a sleeve bearing arrangement comprised of a shaft formed of steel and a sleeve bearing formed of Nylon 66 is fabricated and subjected to a test.

[0041] As the bearing according to the invention is light in weight, and still is able to retain oil and grease for a long duration, it has been confirmed that the invention can provide a maintenance-free sleeve bearing arrangement that does not require resupply of oil during operation. 

What is claimed is:
 1. An bearing arrangement comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing is formed of CRB ceramics.
 2. An bearing arrangement of claim 1, wherein the shaft is formed of a steel-based metal.
 3. An bearing arrangement of claim 1, wherein the shaft is formed of a synthetic resin.
 4. An bearing arrangement of claim 1, wherein the shaft is formed of the CRB ceramics.
 5. An bearing arrangement comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing is formed of a steel-based metal, and the shaft is formed of CRB ceramics.
 6. An bearing arrangement comprised mainly of a shaft and a sleeve bearing, wherein the sleeve bearing is formed of a synthetic resin, and the shaft is formed of CRB ceramics. 